Ni0.6Co0.2Mn0.2(OH)2 Precursor Powder for Single-Crystal NCM622 Cathode Synthesis, 100 g/bottle, CLIBPCSCNCM622OH
Use your own shipping account?
We support FedEx, UPS, and DHL third-party billing for institutional customers.
Place your order first, then email shipping@echemsupplies.com with your account details and order number. We'll generate the label using your account and refund your shipping charges, less a handling fee.
The Ni0.6Co0.2Mn0.2(OH)2 is obtained by co-precipitation method, which can be mixed with lithium salts (eg: Li2CO3, LiOH) to synthesize the single-crystal NCM622 cathode powder. The precursor reacts with the lithium source at temperatures typically between 800-950 degrees to form the final layered oxide cathode material.
| Part Number |
CLIBPCSCNCM622OH (C-LIB-PC-SCNCM622OH) |
| Chemical Composition |
Ni: 39.8 wt%, Co: 12.55 wt%, 11.43 wt% |
| Particle Size Distribution |
D10 = 2.4 um; D50 =3.1 um; D90 = 4.0 um |
| Tap Density | 1.65 g/cm3 |
| Specific Area | 20.69 m2/g |
| Water Level | 0.36 wt% |
Notes: (1) Please store the SCNCM622OH powder in a dry area (glovebox is preferred); (2) The battery powder is highly recommended to be dried at 80-100°C in a vacuum oven for 6-12 h before use.
References:
- L. Liang, et al. Co–precipitation synthesis of Ni0.6Co0.2Mn0.2(OH)2 precursor and characterization of LiNi0.6Co0.2Mn0.2O2 cathode material for secondary lithium batteries, Electrochimica Acta, 2014, 130, 82-89.
- Q. Zhu, et al. Effect of impeller type on preparing spherical and dense Ni1−x−yCoxMny(OH)2 precursor via continuous co-precipitation in pilot scale: A case of Ni0·6Co0·2Mn0·2(OH)2, Electrochimica Acta, 2019, 318, 1-13.